- productspecificaties
- Verpakkingen
- vraag offerte
Type
Stainless steel filler with 13% chromium for overlay welding and joining.
classification
AWS
A 5.9: ER410
EN ISO
14700: S Fe7
14343-A: W Z 13
W.Nr.
1.4009
DIN
8555: TIG 5-GZ-CGTZ
Toepassingen
Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. CEWELD® 410 Tig has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.
Type
Stainless steel filler with 13% chromium for overlay welding and joining.
Toepassingen
Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. CEWELD® 410 Tig has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.
Eigenschappen
CEWELD® 410 Tig is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding.
Classificatie
AWS
A 5.9: ER410
EN ISO
14700: S Fe7
14343-A: W Z 13
F-nr
6
FM
5
W.Nr.
1.4009
DIN
8555: TIG 5-GZ-CGTZ
Geschikt voor
Ferritic 13 % Chrome steel,
1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008, 1.4021, 1.4024,
X6Cr13, X6CrAl13, X10Cr13, X15Cr13, X20Cr13, G-X10Cr13
AISI 410, 420
Goedkeuringen
CE
Lasposities
Hardness
Hardness after PWHT: 180HB
Gas acc. EN ISO 14175
I1
Mechanische waarden
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 420 | 650 | 15 | 35 HRc |