Type
High C-, Cr-, Mo, Nb-, V-, alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear weldable without protective gas.
classification
EN ISO
14700: T Fe16
DIN
8555: MF 10-GF-70-G
Applications
Hardfacing wornout parts that requires maximum hardness in just 1 or 2 layers combined with highest wear resistance.
Type
High C-, Cr-, Mo, Nb-, V-, alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear weldable without protective gas.
Applications
Hardfacing wornout parts that requires maximum hardness in just 1 or 2 layers combined with highest wear resistance.
Propriétés

Extreme good wear resistance even at increased working temperatures. More than 1, maximum 2 layers should not be deposited. A Buffer layer with OA 4370, OA MnCr or ER 100 is recommended. 

Classification
EN ISO
14700: T Fe16
DIN
8555: MF 10-GF-70-G
Convient pour

67-69 HRc hardfacing alloy, for fire gratings, sintering plants, augers and blast furnace bells ,gravel washing equipment, clinker crushers, stone recycling, screw conveyors, sintering lines, mixer blades, wear plates, earth moving equipment etc.

Positions de soudage
PA
PB
Etuvage
140°C / 24 hr
Analyse
C Si Mn Cr Ni Mo Nb Ti V N Fe W B Co Cu Al
4 1.2 0.25 18 0.3 11 0.45 1.8
Propriétés mécaniques
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 69 HRc
fiche produit
déclaration de conformité
FDS
fiche produit
demander un devis
FDS