Type
Stainless steel filler with 13% chromium for overlay welding and joining.
classification
AWS
A 5.9: ER410
EN ISO
14700: S Fe7
14343-A: W Z 13
W.Nr.
1.4009
DIN
8555: TIG 5-GZ-CGTZ
Applications

Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. CEWELD® 410 Tig has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.

Type
Stainless steel filler with 13% chromium for overlay welding and joining.
Applications

Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. CEWELD® 410 Tig has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.

Properties

CEWELD® 410 Tig is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding.

Classification
AWS
A 5.9: ER410
EN ISO
14700: S Fe7
14343-A: W Z 13
F-nr
6
FM
5
W.Nr.
1.4009
DIN
8555: TIG 5-GZ-CGTZ
Suitable for

Ferritic 13 % Chrome steel,

1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008,  1.4021, 1.4024, 

X6Cr13, X6CrAl13,  X10Cr13, X15Cr13, X20Cr13, G-X10Cr13

AISI 410, 420

Approvals
CE
Welding positions
PA
PB
PC
PD
PE
PF
PG
Redrying
Not required
Hardness
Hardness after PWHT: 180HB
Gas acc. EN ISO 14175
I1
Analysis
C Mn Cr Ni Mo Nb V Fe W Co Cu Al Si Ti B N P S
0.02 0.5 13 0.3 0.03
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 420 650 15 35 HRc
Product sheet