Selectarc Cu116
CEWELD®E CuAl8 is an alkaline electrode for bonding aluminum bronzes with an Al content of max. 10 %, as well as for wear-resistant and corrosion-resistant coatings on steel, cast steel and cast iron, especially when exposed to erosion.
by erosion. CEWELD®E CuAl8 is suitable for filling cavities in new aluminum castings, as a buffer layer between Cu and Ni alloys and as a bearing material under high compressive stress.
CEWELD®E CuAl8 is an alkaline electrode for bonding aluminum bronzes with an Al content of max. 10 %, as well as for wear-resistant and corrosion-resistant coatings on steel, cast steel and cast iron, especially when exposed to erosion.
by erosion. CEWELD®E CuAl8 is suitable for filling cavities in new aluminum castings, as a buffer layer between Cu and Ni alloys and as a bearing material under high compressive stress.
The weld metal of CEWELD®E CuAl8 offers good wear and corrosion resistance. The weld metal has good mechanical properties, is acid-resistant and resistant to seawater and erosion.
Welding instructions: - Preheating for sections >6 mm from 150 to 300 ºC is recommended. For thick sheets, a V-seam with a 90° opening angle should be made. Preferably weld in a horizontal position (PA) electrode perpendicular to the workpiece with a short arc, low current and high speed.
Aluminium bronze, Cladding steel, Shafts, Gliding surfaces, Joining steel to, Aluminium Bronze or Copper, etc.
Mat.n: 2.0916, 2.0920, 2.0928, 2.0460, 2.0932
CuAl5, CuAl8, G-CuAl9, CuZn20Al2, CuAl8Fe3,
UNS: C60600, C61000, C68700, C61400, Copper-beryllium alloys Cu+0.5-2%Be, Cu-Zn brasses, Aluminum brass Cu22%, Zn2%Al, Manganese bronzes Cu+20-45%Zn+1-3%Mn, Silicon bronzes Cu+1-3.5%Si
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 200 | 450 | 24 | 150 HB |