Lincoln LNT/LNM 304H
Welding stainless steel types with an alloy content between 16 to 21% Cr and 8 to 13 % Ni, with high carbon content. The names 18-8, 19-9, and 20-10 are often associated with filler metals of this classification.
Welding stainless steel types with an alloy content between 16 to 21% Cr and 8 to 13 % Ni, with high carbon content. The names 18-8, 19-9, and 20-10 are often associated with filler metals of this classification.
CEWELD 308H has been developed for typical operating temperatures up to 400ºC, and up to 600ºC in the short-term range. It also shows good resistance to general corrosion. CEWELD 308H shows higher temperature and scale resistance than the standard L-type. The microstructure is austenite with approx. 5-10% ferrite.
ISO 15608: 8.1 Austenitic ≤ 19 % Cr 9 % Ni, TÜV 1000: Gr. 21,
1.4301, 1.4308, 1.4948, 1.4878, 1.4940, 1.4912, 1.6900, 1.6901, 1.6902, 1.6903, 1.9606
X 5 CrNi 18 10, X 5 CrNi 18 9, G-X 6 CrNi 18 9, X 12 CrNi 18 9, G-X 8 CrNi 18 10, X 6 CrNi 18 10, X 10 CrNiTi 18 10, X 5 CrNi 18 10
AISI 304, 304H, 312, 321H, 347, 347H,
UNS S30409, S32109, S34709, S30400, S32100, S34700
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Impact Energy (J) ISO-V | Hardness | |
|---|---|---|---|---|---|---|
| -40°C | -196°C | |||||
| As Welded | 460 | 640 | 38 | 150 | 90 | HRc |