VAUTID V 146
Hersteller
Ceweld product
Type
High C-, Cr-, Mo, Nb-, V-, alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear weldable without protective gas.
classification
EN ISO
14700: T Fe16
DIN
8555: MF 10-GF-70-G
Anwendungen
Hardfacing wornout parts that requires maximum hardness in just 1 or 2 layers combined with highest wear resistance.
Type
High C-, Cr-, Mo, Nb-, V-, alloyed flux-cored wire electrode which forms extremely hard carbides for extremely hard deposits on parts subject to excessively heavy abrasive wear weldable without protective gas.
Anwendungen
Hardfacing wornout parts that requires maximum hardness in just 1 or 2 layers combined with highest wear resistance.
Eigenschaften
Extreme good wear resistance even at increased working temperatures. More than 1, maximum 2 layers should not be deposited. A Buffer layer with OA 4370, OA MnCr or ER 100 is recommended.
Classification
EN ISO
14700: T Fe16
DIN
8555: MF 10-GF-70-G
Geeignet für
67-69 HRc hardfacing alloy, for fire gratings, sintering plants, augers and blast furnace bells ,gravel washing equipment, clinker crushers, stone recycling, screw conveyors, sintering lines, mixer blades, wear plates, earth moving equipment etc.
Schweißpositionen
Mechanische Gütewerte
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 69 HRc |